Component: Single component engineering mechanical paint made of thermoplastic acrylic resin, pigment and additives.
key characteristics: The paint can be dry quickly at room temperature, no color change to yellow, has high adhesion, good weather resistance, has good stability to wet tropical climate.
main application: Used for coating various metal surfaces, suitable for vehicles, engineering machinery devices and other surfaces for decorative coating usage.
| Item | parameter |
|---|---|
| The appearance of the paint film | meets the standard sample smoothness |
| Viscosity (coated-4) | 80~100s |
| Drying time h（25±1℃） | ≤0.5 ≤6 |
| Cover force g/m2 | ≤ White 110yellow 130 red140 |
| Solid content | ≤50% |
| Flexibility | ≤1mm |
| Hardness | ≥0.5 |
| Adhesion (circle method) | ≤1grade |
| fineness | ≤25μm |
| Moisture resistance（48h） | No foaming, No falling off |
| Water resistance（soak immersion for 24h） | No foaming, No falling off, the adhesion force unchanged |
| Impact resistance | 50kg·cm |
Application parameters：
ratio：single drum
period：unlimited
Diluent and dosage: the special diluent can be adjusted to the application.
Painting method: brushing, rolling coating or spraying Painting
interval: minimum 2 hours, maximum 6 hours
product type:
Komatsu yellow acrylic acid polyester polyurethane magnetic paint / engineering yellow acrylic acid polyurethane magnetic paint / orange yellow acrylic acid polyurethane magnetic paint / orange red acrylic acid polyurethane magnetic
Paint composition:
This product is two-component self-drying engineering machinery coating containing hydroxyacrylic resin, imported pigment, additives, thin ground paint and curing agent.
key Characteristics: The coating combines the high weather resistance of acrylic paint, the excellent adhesion of polyurethane paint, the high decoration of polyester paint, has excellent weather resistance, paint film bright, plump, high hardness.
Has a good light protection, color protection and three protection performance.
main application: Suitable for outdoor excavator crane, bulldozers, loaders, mining machinery and equipment.
Parameter
| Item | parameter | Test method |
|---|---|---|
| The appearance of the paint film | meets the standard sample smoothness | GB1729-79 |
| Viscosity (coated-4) | 80~100 | GB1723-79 |
| Drying time h（25±1℃） | Surface dry≤0.5min Real dry≤24h | GB/T1728-79 |
| fineness | ≤20μm | GB1724-79 |
| Solid content | ≥50% | GB1725-79 |
| Adhesive force | ≤1 | GB/T1720 |
| gloss | ≥93% | GB1743 |
| hardness | ≥0.6 | GB/T6739 |
| Flexibility | ≤1mm | GB/T1731 |
| Water resistance | 240 no change | GB5209 |
| Gasoline resistance | 360 No fall off,No bubble | GB1734 |
Diluent: special dilute material for the polyurethane
Applicable primer: epoxy, polyurethane series all primer, structural paint, two slurry; Storage stability: 12 months Painting method: brush coating, tut coating, electrostatic spraying.